This is a multi-layer material designed for electrostatic and moisture protection in ESD and moisture barrier packaging.
Its structure, composed of polyester, aluminum foil, polyamide, and polyethylene, is engineered to meet the requirements of a wide range of applications.
Feature:- Complies with ANSI/ESD S20.20 2021
- Stable ~4.12 E10 Ω (@12% RH)
- ESD energy penetration < 10 nJ
- At 12% RH, triboelectric voltage is effectively controlled at 84 V
- Amine-free / amide-free
| Kenner Film Series |
Physical Properties | Surface Resistivity | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Film Thickness (mm) |
Base Polymer | Tensile Strength (MD/TD) kg/cm2 |
Elongation (MD/TD) % |
Haze % |
Puncture Strength Kgf |
outer at 23°C X 50% RH ohms |
inner at 23°C X 50% RH ohms |
|||
| Test Method | Thickness Gauge |
ASTM D-882 | ASTM D-882 | ASTM D1003 | FTMS 101C Method 2065.1 |
ANSI/ESD STM11.11 STM11.13 |
ANSI/ESD STM11.11 STM11.13 |
|||
|
Kenner Film Series
KF-1460
|
Physical Properties |
Film Thickness (mm)
80
Test Method: Thickness Gauge
|
Base Polymer
Polyolefin/ PA
|
Tensile Strength (MD/TD) kg/cm2
> 220
Test Method: ASTM D-882
|
Elongation (MD/TD) %
> 300
Test Method: ASTM D-882
|
Haze %
< 40
Test Method: ASTM D1003
|
Puncture Strength Kgf
> 3
Test Method: FTMS 101C Method 2065.1
|
Surface Resistivity |
outer at 23°C X 50% RH ohms
≦ 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
inner at 23°C X 50% RH ohms
≦ 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
|
Kenner Film Series
KF-1605D
|
Physical Properties |
Film Thickness (mm)
75
Test Method: Thickness Gauge
|
Base Polymer
PE/ Antistatic PE
|
Tensile Strength (MD/TD) kg/cm2
200 / 140
Test Method: ASTM D-882
|
Elongation (MD/TD) %
500
Test Method: ASTM D-882
|
Haze %
Test Method: ASTM D1003
|
Puncture Strength Kgf
Test Method: FTMS 101C Method 2065.1
|
Surface Resistivity |
outer at 23°C X 50% RH ohms
≦ 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
inner at 23°C X 50% RH ohms
≦ 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
|
Kenner Film Series
KF-1606SP
|
Physical Properties |
Film Thickness (mm)
90
Test Method: Thickness Gauge
|
Base Polymer
PE/ Antistatic PE
|
Tensile Strength (MD/TD) kg/cm2
170
Test Method: ASTM D-882
|
Elongation (MD/TD) %
500
Test Method: ASTM D-882
|
Haze %
Test Method: ASTM D1003
|
Puncture Strength Kgf
2.5
Test Method: FTMS 101C Method 2065.1
|
Surface Resistivity |
outer at 23°C X 50% RH ohms
PE Layer: < 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
inner at 23°C X 50% RH ohms
PE Layer: < 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
|
Kenner Film Series
KF-1608AS
|
Physical Properties |
Film Thickness (mm)
20
Test Method: Thickness Gauge
|
Base Polymer
PE/ Antistatic PE
|
Tensile Strength (MD/TD) kg/cm2
> 200
Test Method: ASTM D-882
|
Elongation (MD/TD) %
> 300
Test Method: ASTM D-882
|
Haze %
Test Method: ASTM D1003
|
Puncture Strength Kgf
Test Method: FTMS 101C Method 2065.1
|
Surface Resistivity |
outer at 23°C X 50% RH ohms
PE Layer: < 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|
inner at 23°C X 50% RH ohms
PE Layer: < 9E10
Test Method: ANSI/ESD STM11.11 STM11.13
|